A sustainable water-resistant coating based on a chitosan/sacred lotus leaf wax composite was developed and deposited onto cotton fabrics using a simple dip–dry–cure process. The effect of the chitosan-to-sacred lotus leaf wax weight ratio on the surface wettability, air permeability, water vapor permeability, mechanical properties, and laundering durability of the coated fabrics was systematically investigated. The incorporation of sacred lotus leaf wax significantly enhanced the hydrophobicity of the cotton fabrics, with the highest water contact angle (WCA) of 167.12° achieved at a chitosan-to-wax weight ratio of 7:3. Although increasing the wax content improved water repellency, it also resulted in slight reductions in tensile strength, air permeability, and water vapor permeability. After 20 home-machine washings, the coated fabric retained a WCA of 137.11°, demonstrating good laundering durability. These results demonstrate that the chitosan/sacred lotus leaf wax composite is a biodegradable, non-toxic, and environmentally friendly alternative to conventional water-repellent finishes, offering considerable potential for the development of sustainable functional textile coatings.
เหตุผลที่อยู่ในฐานติดตาม
ระเบียนนี้ได้รับ Impact Signal 71/100 จากความใหม่ แหล่งเผยแพร่ ความร่วมมือ และสัญญาณในข้อมูลบรรณานุกรม คะแนนนี้ใช้จัดลำดับการติดตาม ไม่ใช่การตัดสินคุณภาพงานวิจัย
ประเด็นที่เกี่ยวข้อง: Surface Modification and Superhydrophobicity · Nanocomposite Films for Food Packaging · Dyeing and Modifying Textile Fibers
บทบาทของนักวิจัยและสถาบันไทย
Walaikorn Nitayaphat · Kageeporn Wongpreedee · Thanut Jintakosol · Srinakharinwirot University
ข้อจำกัดของข้อมูล
หน้านี้เป็นระเบียนบรรณานุกรมและข้อมูลจากบทคัดย่อ ยังไม่ใช่บทวิเคราะห์ฉบับเต็มหรือการประเมินคุณภาพงานวิจัย ควรตรวจสอบ DOI และเอกสารต้นฉบับก่อนนำไปอ้างอิง