Recycled aggregate concrete (RAC) reuses demolition waste, but its porous aggregate and weak interfacial zones make it vulnerable to freeze–thaw damage in cold regions. This study asked whether multi-scale hybrid reinforcement can close this durability gap, and at which whisker dosage. Basalt fiber (BF) bridges macro-scale cracks and calcium carbonate whisker (CW) fills pores and restrains microcracks, acting at different scales and damage stages. Six mixtures with 25% pretreated recycled aggregate, 0.1 vol.% BF, and 0.1–0.5 vol.% CW underwent 300 freeze–thaw cycles and were assessed by mass loss, dynamic modulus, compressive strength, SEM, and MIP. At 0.3 vol.% CW, mass loss fell by 87.1%, 72.10% of the dynamic modulus was retained, and damage was limited to D = 0.28; 0.5 vol.% CW caused agglomeration. Reinforcement added about 3% embodied carbon and cut durability-normalized carbon intensity by 69%. The results yield a dosage-based design rule; aggregate treatment alone is insufficient.
เหตุผลที่อยู่ในฐานติดตาม
ระเบียนนี้ได้รับ Impact Signal 73/100 จากความใหม่ แหล่งเผยแพร่ ความร่วมมือ และสัญญาณในข้อมูลบรรณานุกรม คะแนนนี้ใช้จัดลำดับการติดตาม ไม่ใช่การตัดสินคุณภาพงานวิจัย
ประเด็นที่เกี่ยวข้อง: Recycled Aggregate Concrete Performance · Innovative concrete reinforcement materials · Structural Behavior of Reinforced Concrete
บทบาทของนักวิจัยและสถาบันไทย
Kai Li · Kamtornkiat Musiket · Boonchai Phungpaingam · Supasit Pongsivasathit · Rajamangala University of Technology
ข้อจำกัดของข้อมูล
หน้านี้เป็นระเบียนบรรณานุกรมและข้อมูลจากบทคัดย่อ ยังไม่ใช่บทวิเคราะห์ฉบับเต็มหรือการประเมินคุณภาพงานวิจัย ควรตรวจสอบ DOI และเอกสารต้นฉบับก่อนนำไปอ้างอิง